Product: Double Faced Tape #5782
- Product Overview
SEKISUI #5782 is a double-sided adhesive tape developed for:
- Resin parts such as polypropylene (PP)
- Polyurethane foam materials
It features:
- Low total VOC emissions
- Low odor, suitable for enclosed environments such as vehicle interiors
- Applications
- Fixing industrial components
- Fixing interior parts
- Bonding foam materials in HVAC systems
- Features
- (1) Significantly lower total VOC emissions compared to conventional products
- (2) Low odor, providing a more comfortable environment in enclosed spaces
- (3) Excellent adhesion to polyolefin materials such as PP
- (4) Free from 13 hazardous substances regulated by the Japanese Ministry of Health, Labour and Welfare
Restricted substances (not included):
- Formaldehyde
- Toluene
- Xylene
- Chlorpyrifos
- p-Dichlorobenzene
- Ethylbenzene
- Styrene
- Dibutyl phthalate
- Diethylhexyl phthalate
- Tetradecane
- Diazinon
- Acetaldehyde
- Fenobucarb
- Structure
- Acrylic adhesive
- Non-woven fabric
- Acrylic adhesive
- Release liner
- Standard Size
- Thickness: 0.130 mm
- Width: 1000 mm
- Length: 50 m
(Other sizes are available upon request)
- Technical Properties
180° Peeling Adhesion (23°C)
(Based on JIS Z 0237)
| Substrate | Value (N/25mm) |
| SUS | 19.2 |
| PP | 15.2 |
| PS | 19.5 |
| PET | 21.5 |
| ABS | 19.1 |
| PC | 22.1 |
| AL | 18.1 |
Holding Power
- 40°C / 1 kg / 1 hour
- 80°C / 0.5 kg / 1 hour
- Adhesion vs Temperature
| Temperature | Adhesion (N/25mm) |
| 0°C | 26.2 |
| 23°C | 18.2 |
| 40°C | 22.5 |
| 60°C | 14.3 |
| 80°C | 7.8 |
- Mechanical Properties
Shear Strength
| Temperature | N/cm² |
| 5°C | ≥100 |
| 23°C | 22.5 |
| 40°C | 24.8 |
Tensile Strength
| Temperature | N/cm² |
| 5°C | 41.4 |
| 23°C | 31.1 |
| 40°C | 33.5 |
- Durability Performance
| Condition | Adhesion (N/25mm) |
| Initial (23°C, 50% RH) | 18.2 |
| Low temperature (-30°C, 14 days) | 18.4 |
| High temperature (80°C, 14 days) | 18.9 |
| High temp & humidity (60°C, 90%, 14 days) | 18.6 |
| Thermal cycle (-30 ⇔ 80°C, 300 cycles) | 18.4 |